Nonwoven polyolofin ve doğal keten/jüt takviyeli hibrit kompozitlerde iki farklı nonwoven üretim yönteminin malzemenin mekanik özelliklerine etkisi

Basit Öğe Kaydı
dc.contributor.advisorSayer, Sami
dc.contributor.authorKocamış, Uğur Ömer
dc.date.accessioned2020-12-22T12:01:11Z
dc.date.available2020-12-22T12:01:11Z
dc.date.issued2019en_US
dc.date.submitted2019
dc.departmentFen Bilimleri Enstitüsüen_US
dc.description.abstractBu çalışmada doğal lif takviyeli hibrit kompozitlerin mekanik özellikleri üzerinde hibrit liflerin ve matris malzemesi olan nonwoven kumaşların farklı üretim yöntemi ile imal edilmiş olmasının etkisinin analizine odaklanmıştır. Doğal hibrit takviyeli ve polimer matrisli kompozit numuneler üretilerek mekanik özellikleri incelenmiştir. Takviye elemanları olarak jüt ve keten kumaşları kullanılırken, matris elemanı olarak polietilen (PE) film ve polipropilen (PP) nonwoven kumaşlar seçilmiştir. Polipropilen nonwoven kumaşların üretim yöntemleri meltblown ve spunbond olarak farklı iki kategoriden seçilmiştir. Deney sonuçlarının sağlamasını daha güvenilir yapmak adına farklı yoğunluk seviyelerindeki nonwoven kumaşlar kullanılarak deney farklı seviyelerde mukayese edilmiştir ve ayrıca farklı kütle/alan özelliğine sahip nonwoven kumaşların da kompozit malzemeye olan etkisi incelenmiştir. Jüt ve keten kumaşlarının yüzeyi, matrisi ile uyumluluğu arttırmak için alkali işlemle modifiye edilmiştir. Hibrit kompozitleri karakterize etmek için ASTM ve DIN standartlarına göre deneysel çekme, eğilme ve darbe testleri yapılmıştır. Son olarak, test edilen numunelerin kırılma yüzeyini incelemek için bir taramalı elektron mikroskobu (SEM) kullanılmıştır. Bulgular üretilen kompozit numunelerin saf HDPE ile kıyaslandığında dayanımı arttırtığını göstermektedir. Fakat kompozit numunelerin kendi içersinde kıyaslanması, Spunbond yöntemi ile üretilen nonwoven yüzeyli hibrit kompozitlerin Meltblown ile üretilenlerden daha mukavim olduğu ve sonuçlarının daha stabil olduğunu ortaya koymaktadır. Ayrıca gramaj farkının SB numunelerinde ters orantılı bir etkiye sebep olduğu, MB numunelerinde ise ayırt edici bir özellik olmadığı gözlemlenmiştir.en_US
dc.description.abstractThe present study is focused on the analysis of the effect of hybridization and the effect of two different manufacturing methods for nonwoven polymer matrix on the mechanical properties of natural fiber-reinforced hybrid composites. Natural fiber-reinforced hybrid composite samples with polymer matrix were manufactured and mechanical properties were investigated. Reinforcement materials were jute and flax, matrix polymers were polyethylene films and nonwovens made of polypropylene. PP nonwovens were manufactured by two different method which were meltblown and spunbond. Several densities of nonwovens were used for reliable experiment results and also effect of different mass/area ratio nonwovens on mechanical properties of composite material was investigated. The surface of jute and flax reinforcements has been modified by alkali treatment in order to enhance the compatibility with the matrix. Experimental tensile, flexural and impact tests were performed according to ASTM and DIN standards to characterize the new intralaminar hybrid composites. Finally, a scanning electron microscopy (SEM) was used to examine the fracture surface of the tested specimens. The results indicates that the composite samples increase the strength compared to pure HDPE. However, the comparison of composite samples among themselves shows that hybrid composites by Spunbond nonwoven method are more durable and stable than those produced by Meltblown. In addition, it was observed that the weight difference caused an inversely proportional effect in the SB samples, but it was not a distinguishing feature in the MB samples.en_US
dc.identifier.urihttps://hdl.handle.net/11454/68272
dc.language.isotren_US
dc.publisherEge Üniversitesi, Fen Bilimleri Enstitüsüen_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectHibriten_US
dc.subjectKompoziten_US
dc.subjectMeltblownen_US
dc.subjectSpunbonden_US
dc.subjectNonwovenen_US
dc.subjectPPen_US
dc.subjectPEen_US
dc.subjectPolipropilenen_US
dc.subjectPolietilenen_US
dc.subjectMekanik Özelliken_US
dc.subjectHybriden_US
dc.subjectCompositeen_US
dc.subjectMeltblownen_US
dc.subjectSpunbonden_US
dc.subjectNonwovenen_US
dc.subjectPolypropyleneen_US
dc.subjectPolyethyleneen_US
dc.subjectMechanical Propertiesen_US
dc.titleNonwoven polyolofin ve doğal keten/jüt takviyeli hibrit kompozitlerde iki farklı nonwoven üretim yönteminin malzemenin mekanik özelliklerine etkisien_US
dc.title.alternativeEffect of two different nonwoven manufacturing method on mechanical properties of nonwoven polyolofin and natural flax/jute reinforced hybrid compositesen_US
dc.typeMaster Thesisen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
uguromerkocamis2019.pdf
Boyut:
10.59 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Yüksek lisans tez dosyası
İndir
Lisans paketi
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
license.txt
Boyut:
1.44 KB
Biçim:
Item-specific license agreed upon to submission
Açıklama:
İndir

Koleksiyon

Fen Bilimleri Enstitüsü Tez Koleksiyonu