Çelik lifli betonların darbe direncine agrega maksimum boyutunun etkisi

Basit Öğe Kaydı
dc.contributor.authorŞemsi Yazıcı
dc.contributor.authorGözde İnan Sezer
dc.date.accessioned2019-10-26T19:40:24Z
dc.date.available2019-10-26T19:40:24Z
dc.date.issued2008
dc.departmentEge Üniversitesien_US
dc.description.abstractBu çalısmada çelik lifli betonların darbe direncine, agrega maksimum dane boyutunun etkisi incelenmistir. Çalısmada maksimum dane boyutu 10 mm, 15 mm, 20 mm ve 25 mm olan kireç tası kökenli kırma agrega kullanılarak, 8 farklı lifsiz-çelik lifli beton üretilmistir. Üretilen lifli-lifsiz betonlarda; su/çimento oranı 0.50, çimento dozajı 400 kg/m3 olarak sabit tutulmustur. Lifli betonlarda hacimce % 1.0 oranında, narinligi 65 olan, iki ucu çengelli çelik lif kullanılmıstır. Üretilen betonlardan hazırlanan 150 mm ayrıtlı küp örnekler üzerinde, 28 günlük standart kür sonunda tek eksenli basınç, yarmada çekme ve ultra ses deneyleri yapılarak, betonların mekanik özellikleri belirlenmistir. Ayrıca, çalısma kapsamında üretilen betonların darbe testleri ACI 544.3R-93 ‘ce önerilen darbe deney düzeneği kullanılarak gerçeklestirilmistir. Darbe testleri için 150 mm çaplı 300 mm yükseklikli örnekler hazırlanarak 28 gün kür edildikten sonra, çapı 150 mm yüksekliği 64 mm olacak sekilde kesilerek özel diskler hazırlanmıs ve bu diskler üzerinde darbe testleri yapılmıstır. Deneylerden elde edilen sonuçlar lif varlıgı ve agrega maksimum boyutunun değisimine bağlı olarak değerlendirilmistir.en_US
dc.description.abstractIn this study, the effect of maximum size of aggregate on impact resistance of fiber reinforced concrete were investigated. Using crushed limestone aggregate with 10, 15, 20 and 25 mm of maximum size, 8 different normal-steel fiber reinforced concretes were produced. Water/cement ratio and cement dosage of concrete mixtures are 0.5 and 400 kg/m3, respectively. Hooked-end bundled steel fibers with l/d ratio of 65 and 1.0% fiber volume were used in fiber concretes. After 28 days standard curing, compressive strength, split tensile strength and ultrasonic pulse velocity tests were performed on 150/150/150 mm cube specimens. Additionally, impact resistances of concrete specimens were determined using impact test apparatus described in ACI 544.3R-93. 150x300 mm cylinders were prepared for impact resistance tests. After 28 days curing, these specimens were cut and 150x64 mm special discs were prepared. Impact resistance test were performed on these special discs. Experimental results were evaluated corresponding to presence of steel fiber and aggregate maximum size.en_US
dc.identifier.endpage245en_US
dc.identifier.issn1300-7009
dc.identifier.issue3en_US
dc.identifier.startpage237en_US
dc.identifier.urihttps://app.trdizin.gov.tr/makale/T0RNd05qazU=
dc.identifier.urihttps://hdl.handle.net/11454/11874
dc.identifier.volume14en_US
dc.indekslendigikaynakTR-Dizinen_US
dc.language.isotren_US
dc.relation.ispartofPamukkale Üniversitesi Mühendislik Fakültesi Mühendislik Bilimleri Dergisien_US
dc.relation.publicationcategoryDiğeren_US]
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectMühendisliken_US
dc.subjectOrtak Disiplinleren_US
dc.titleÇelik lifli betonların darbe direncine agrega maksimum boyutunun etkisien_US
dc.title.alternativeThe effect of aggrega te maximum size on impact resistance of fiber reinforced concreteen_US