    Polymeric thermal analysis of C+H and C+H+Ar ion implanted UHMWPE samples
    (Elsevier Science Bv, 2007) Kaya, N.; Oztarhan, Ahmet M.; Urkac, E. S.; Ila, D.; Budak, S.; Oks, E.; Nikolaev, A.; Ezdesir, A.; Tihminlioglu, F.; Tek, Z.; Cetiner, S.; Muntele, C.
    Chemical surface characterization of C + H hybrid ion implanted UHMWPE samples were carried out using DSC (differential scanning calorimeter) and TGA (thermal gravimetric analysis) techniques. Samples were implanted with a fluence of 10(17) ion/cm(2) and an extraction voltage of 30 kV. The study of TGA and DSC curves showed that: (1) Polymeric decomposition temperature increased, (2) T-m, Delta C-p and Delta H-m values changed while Delta C-p and Delta H-m increased. T-g value could not be measured, because of some experimental limitations. However, the increase in Delta H-m values showed that T-g values increased, (3) the branch density which indicated the increase in number of cross-link (M-c) decreased in ion implanted samples and (4) increase in Delta H-m values indicated increase in crystallinity of implanted surface of UHMWPE samples. Published by Elsevier B.V.
  • Küçük Resim Yok
    Öğe
    Thermal characterization of Ag and Ag plus N ion implanted ultra-high molecular weight polyethylene (UHMWPE)
    (Elsevier Science Bv, 2007) Urkac, E. Sokullu; Oztarhan, A.; Tihminlioglu, F.; Kaya, N.; Ila, D.; Muntele, C.; Budak, S.; Oks, E.; Nikolaev, A.; Ezdesir, A.; Tek, Z.
    Most of total hip joints are composed of ultra-high molecular weight polyethylene (UHMWPE). However, as ultra-high molecular weight polyethylene is too stable in a body, wear debris may accumulate and cause biological response such as bone absorption and loosening of prosthesis. In this study, ultra-high molecular weight polyethylene samples were Ag and Ag + N hybrid ion implanted by using MEVVA ion implantation technique to improve its surface properties. Samples were implanted with a fluence of 10(17) ion/cm(2) and extraction voltage of 30 kV. Implanted and unimplanted samples were investigated by thermo-gravimetry analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), optical microscopy (OM) and contact Angle measurement. Thermal characterization results showed that the ion bombardment induced an increase in the % crystallinity, onset and termination degradation temperatures of UHMWPE. (c) 2007 Elsevier B.V. All rights reserved.