    The effects of crosslinker ratio and photoinitiator type on the properties of pnipam hydrogel
    (Springer, 2023) Oral, Nur; Basal, Guldemet
    In this study, Poly(N-isopropylacrylamide) (PNIPAM) hydrogels were produced from N-isopropylacrylamide (NIPAM), at three different concentrations of crosslinker, N,N & PRIME;-methylenebisacrylamide (BIS) (0.50%, 0.35%, and 0.25%) using two types of photoinitiator, a hydrophilic photoinitiator (Irgacure 2959) and a hydrophobic photoinitiator (Irgacure 651). When Irgacure 651 was used photopolymerization process was completed in 20 min compared to two hours with Irgacure 2959. However, the resultant hydrogels were opaque suggesting a heterogeneous structure, which in turn led to low compressive strength. Besides, when hydrogel solution was prepared with Irgacure 651 in water/ethanol mixture 0.25% crosslinker ratio was not sufficient to form a hydrogel. Irgacure 2959 produced homogenous transparent hydrogels with a higher degree of swelling. When the crosslinker ratio decreased swelling capacity increased, but hydrogels became weaker. The decrease in compressive strength was particularly high at the 0.25% crosslinker ratio. The crosslinker ratio or photoinitiator type did not have any significant effect on the phase transition temperature. On the other hand, hydrogel samples prepared with Irgacure 651 in water/ethanol mixture showed a quicker response to swelling and deswelling. In conclusion, in terms of morphology, swelling capacity, and compressive strength the best results were obtained with the crosslinker ratio of 0.35% and Irgacure 2959.
  • Küçük Resim Yok
    Öğe
    A Hydrophilic/Hydrophobic Composite Structure for Water Harvesting from the Air
    (E.U. Printing And Publishing House, 2022) Basal, Guldemet; Oral, Nur
    The freshwater shortage is one of the world's most pressing challenges needs to be addressed rapidly. To overcome this challenge, harvesting water from the air has emerged as a simple and cost-effective approach. Traditional wire meshes have been already used for atmospheric water harvesting from the fog. In foggy areas, the wire meshes are placed perpendicular to wind and water droplets in fog carried by the wind are trapped and deposited on the surface of meshes. The purpose of this study is to improve the water harvesting capacity of the traditional wire mesh by modifying its surface using a nature-inspired composite structure consisting of hydrophilic and hydrophobic zones. Hydrophilic zones were obtained by electrospinning or electrospraying of the polyamide 6 (PA6) / chitosan (CH) blend, and hydrophobic zones were attained by electrospraying of polycaprolactone (PCL). The water harvesting capacity of the resulting meshes was tested and compared with each other. The highest water harvesting capacity was achieved with the PA6/CH nanofiber coated wire mesh as 87 mg / cm2/h. This mesh collected twice as much water compared to the uncoated mesh. However, its water collection rate decreased when nanofiber surface reached the saturation level. The addition of hydrophobic PCL particles onto PA6/CH nanofibers significantly reduced the amount of water captured. When both PA6/CH and PCL were electrosprayed on the wire mesh in particle form water harvesting capacity slightly increased, but it was still poor compared to uncoated mesh.
  • Küçük Resim
    Öğe
    Yağ-su ayrımında kullanılmak üzere sıcaklık duyarlı akıllı membran geliştirilmesi
    (Ege Üniversitesi, Fen Bilimleri Enstitüsü, 2022) Oral, Nur; Başal Bayraktar, Güldemet
    Bu tez çalışmasında, yağlı su atıklarının arıtılmasında kullanılan membranlarda karşılaşılan körlenme problemine çözüm olabilecek ve membran performansını arttıracak bir malzeme geliştirilmesi amaçlanmıştır. Elektro lif çekim ve elektro püskürtme yöntemlerinin eş zamanlı kullanılmasıyla selüloz asetat (CA) nanolifleri ve poli(N-izopropilakrilamid) (PNIPAM) hidrojel partiküllerinden oluşan kompozit bir membran üretilmiştir. Foto-polimerizasyon yöntemi ile başarıyla üretilen PNIPAM hidrojellerinde maksimum %2846 şişme kapasitesine ulaşılmıştır. Ayrıca, değişen çapraz bağlayıcı oranının ve foto-başlatıcı tipinin hidrojellerin şişme kapasitesine olan etkisi detaylı olarak incelenmiştir. Sıcaklık duyarlı bir malzeme olan PNIPAM hidrojelinin değişen ortam koşullarında gösterdiği davranışlar incelenmiştir. Kompozit membran üretiminden önce, lif ve partiküllerin eldesi için çalışılması gereken işlem parametrelerinin belirlenmesi amacıyla detaylı bir çalışma yapılmıştır. Boncuksuz yapıda selüloz asetat nanolifleri ve nano/mikro boyutta PNIPAM partikülleri başarıyla üretilmiştir. Üretilen kompozit membranların karakteristik özellikleri taramalı elektron mikroskobu (SEM), termogravimetrik analiz (TGA), yüzey temas açısı, cıva porozimetresi ve çekme testi ile incelenmiştir. Sonuç olarak, PNIPAM partiküllerinin selüloz asetat nanolifleri arasına dahil edildiği kompozit bir membran başarıyla üretilmiştir. Üretilen CA/PNIPAM membranının yağ-su karışımı ve yağ-su emülsiyonlarının ayrımında etkinliği ispatlanmıştır. Körlenme direnci arttırılan kompozit membran, sıcaklık duyarlı hidrojel içermesi sayesinde körlenme gerçekleştiğinde kolayca temizlenebilecektir.